ABSplus™ – P430 for Fortus 3D Production Systems

Stratasys ABSplus-P430 is a true production-grade thermoplastic and is an ideal material for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. The marriage of ABSplus-P430 with Fortus 3D Production Systems gives you the ability to create real parts directly from digital files that are stronger, smoother and with high feature detail.

Mechanical Properties1

Test Method

English

Metric

Tensile Strength (Type 1, 0.125″, 0.2″/min) ASTM D638 5,300 psi 37 MPa
Tensile Modulus (Type 1, 0.125″, 0.2″/min) ASTM D638 330,000 psi 2,320 MPa
Tensile Elongation (Type 1, 0.125″, 0.2″/min) ASTM D638 3% 3%
Flexural Delamination ASTM D790 4,500 psi 31 MPa
Flexural Strength (Method 1, 0.05″/min) ASTM D790 7,600 psi 53 MPa
Flexural Modulus (Method 1, 0.05″/min) ASTM D790 320,000 psi 2,250 MPa
IZOD Impact, notched (Method A, 23°C) ASTM D256 2.0 ft-lb/in 106 J/m

Thermal Properties2

 Test Method

English

Metric

Heat Deflection (HDT) @ 66 psi ASTM D648 204°F 96°C
Heat Deflection (HDT) @ 264 psi ASTM D648 180°F 82°C
Coefficient of Thermal Expansion ASTM E831 4.90 E -05 in/in/°F – – – – –
Melt Point – – – – – – – – – Not Applicable3 Not Applicable3

Electrical Properties4

 Test Method

Value Range

Volume Resistivity ASTM D257 3.0x10e14 – 6.0x10e13 ohms
Dielectric Constant ASTM D150-98 2.9 – 2.6
Dissipation Factor ASTM D150-98 .0053 – .0046
Dielectric Strength ASTM D149-09, Method A 320 – 100 V/mm
Dielectric Strength IEC 60112 28.0 kV/mm

Other2

 Test Method

Value

Specific Gravity ASTM D792 1.04

System Availability

Layer Thickness Capability

 Support Structure

 Available Colors

Fortus 250mc 0.013 inch (0.330 mm)

0.010 inch (0.254 mm)

0.007 inch (0.178 mm)5
Soluble Supports Ivory
White
Black
Dark Grey
Red
Blue
Olive Green
Nectarine
Fluorescent Yellow
Custom Colors

The information presented are typical values intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. End-use material performance can be impacted (+/-) by, but not limited to, part design, end-use conditions, test conditions, color etc. Actual values will vary with build conditions. Product specifications are subject to change without notice.

1 Build orientation is on side long edge.
2 Literature value unless otherwise noted.
3 Due to amorphous nature, material does not display a melting point.
4 All Electrical Property values were generated from the average of test plaques built with default part density (sparse). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation.